Ultra stable cementitious construction material formulation

ABSTRACT

A ultrastable cementitious material with nano-molecular veneer makes a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, with 14 wt % to 18 wt % of a magnesium chloride dissolved in water and reacting to form a liquid suspension, mixing from 2 to 10 minutes, adding a phosphorus-containing material, and allowing the liquid suspension to react into an amorphous phase cementitious material, wherein a portion of the amorphous phase cementitious material grows a plurality of crystals. The plurality of crystals are encapsulated by the amorphous phase cementitious material forming a nano-molecular veneer.

CROSS REFERENCE TO RELATED APPLICATIONS

The present application claims priority to and the benefit of U.S. Provisional Patent Application Ser. No. 62/582,517 filed on Nov. 7, 2017, entitled “PROCESS FOR MAKING A CEMENTITIOUS CONSTRUCTION MATERIAL” (our reference 2219.002) and U.S. Provisional Patent Application Ser. No. 62/582,545 filed on Nov. 7, 2017, entitled “CEMENTITIOUS CONSTRUCTION MATERIAL” (our reference 2219.003). These references are hereby incorporated in its entirety.

FIELD

The present embodiment generally relates to a formulation for making an ultra-stable cementitious material.

BACKGROUND

A need exists for a crystalline silica-free construction material with structural integrity, fire-resistance, excellent insulation properties and superior resistance to mold, mildew, and termites.

A further need exists for a construction material with high hot water stability.

The present embodiments meet these needs.

BRIEF DESCRIPTION OF THE DRAWINGS

The detailed description will be better understood in conjunction with the accompanying drawings as follows:

FIG. 1A-1D depicts the stepwise process for making a cementitious material.

FIG. 2 depicts the X-ray diffraction pre-treatment and post-treatment of magnesium oxychloride with phosphoric acid.

FIG. 3A-3H depicts a table of cementitious material formulations containing reinforcing components and aggregate and other additives along with physical properties of the formulations.

FIG. 4 is a table showing various additional formulations made according to the process.

The present embodiments are detailed below with reference to the listed Figures.

DETAILED DESCRIPTION OF THE EMBODIMENTS

Before explaining the present process in detail, it is to be understood that the formulation is not limited to the particular embodiments and that it can be practiced or carried out in various ways.

The invention relates to a process for making an ultra-stable cementitious construction material consisting of a crystallized portion with an amorphous nano-molecular veneer substantially free of crystalline silica.

The first step of the process involves forming a gel phase by blending together magnesium oxide and magnesium chloride in a water with a weight ratio of from 1.9:1 to 2.1:1 of magnesium oxide to magnesium chloride.

In the process, from 2 weight percent to 30 weight percent of aggregate is added to the gel phase, forming an amorphous phase.

Phosphorous acid or phosphoric acid or both are then added to the amorphous phase, actuating crystallization of a portion of the amorphous phase, while simultaneously forming a nano-molecular veneer encapsulating the crystallized portion of the amorphous phase without detectable magnesium phosphate and with from 2% to 49% increase in surface area as compared to veneer-free crystallized portions, and wherein the crystallized portion with nano-molecular veneer is configured to resist degradation in water having a temperature at 60 degrees C. for 48 hours.

Benefits of the process are as follows: increased cement stability when submerged in water at temperatures up to 60 degrees C.; a physical property that determines warm water stability for the above cement and no additional time required for this invention.

Benefits of the cementitious material formulation include increased cement stability when submerged in water at temperatures up to 60 degrees C.

The invention provides magnesium oxychloride cement that has increased stability in environments with high temperatures and high moisture.

The invention provides a cementitious material with a protective layer that is not an exposed crystal, so it is not susceptible to moisture or water dissolving at elevated temperatures.

The invention stabilizes the concrete thereby reducing the corrosion effects on other building materials in the assembly.

This invention has an improved water tolerance over other types of magnesium oxychloride cements without adding polymers or other sealants that can sacrifice some of the excellent fire-resistant properties of magnesium oxychloride cements.

The inventive and unexpected amorphous layer that protects the magnesium oxychloride cement crystals is less detrimental to the structural strength of the cement product than other uses of phosphoric compounds have proven to be.

The invention relates to a process for making a cementitious construction material consisting of a crystallized portion with an amorphous nano-molecular veneer substantially free of crystalline silica.

The first step of the process involves forming a gel phase by blending together magnesium oxide and magnesium chloride in a water with a weight ratio of from 1.9:1 to 2.1:1 of magnesium oxide to magnesium chloride.

In the process, from 2 weight percent to 30 weight percent of aggregate is added to the gel phase, forming an amorphous phase.

Phosphorous acid or phosphoric acid or both are then added to the amorphous phase, actuating crystallization of a portion of the amorphous phase, while simultaneously forming a nano-molecular veneer encapsulating the crystallized portion of the amorphous phase without detectable magnesium phosphate and with a 2% to 49% increase in surface area as compared to veneer-free crystallized portions, and wherein the crystallized portion with nano-molecular veneer is configured to resist degradation in water having a temperature at 60 degrees C. for 48 hours.

Benefits of the process are as follows: increased cement stability when submerged in water at temperatures up to 60 degrees C., a physical property that determines warm water stability for the above cement, and no additional time required for this invention.

The invention relates to an ultrastable cementitious material with nano-molecular veneer.

The ultrastable cementitious material contains 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material, the magnesium oxide with a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles are less than or equal to about 40 microns.

The ultrastable cementitious material contains 14 wt % to 18 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

The ultrastable cementitious material contains 0.1 wt % to 10 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material.

The stabilizing material with the phosphorus-containing compound has a phosphorous acid (A) based on the final total weight of the cementitious material, wherein the phosphorous acid consists of an aqueous solution of 55 wt % to 65 wt % of a concentrate of H₃PO₃; or a phosphoric acid (B) based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

A portion of the amorphous phase cementitious material grows a plurality of crystals, each crystal having a MW within the range of 280 to 709, the amorphous phase cementitious material encapsulating the plurality of crystals, wherein a majority of stabilizing material with a phosphorus-containing compound are consumed into a nano-molecular veneer while increasing surface area of the plurality of crystals by 2% to 49% during curing, and wherein the nano-molecular elements of the cured nano-molecular veneer are insoluble in water and the cured nano-molecular veneer protects the plurality of crystals from degradation in water at temperatures from 20 degrees to 60 degrees Celsius for from 24 hours to 56 days of the formed cementitious material.

In an embodiment, ultra-stable cementitious material with nano-molecular veneer includes: 0.1 wt % to 30 wt % of an aggregate based on a final total weight of the concrete, the aggregate comprising particles, having a diameter from 1 nm to 10 mm, wherein the aggregate comprises at least one of: wood, perlite, styrene based foam beads, calcium carbonate powder, glass particulate, and combinations thereof.

In an embodiment, ultra-stable cementitious material with nano-molecular veneer includes: 0.1 wt % to 2 wt % of a reinforcing material based on a final total weight of the cementitious material, the reinforcing material comprising a non-woven or woven silica containing mat, a non-woven or woven hydrocarbon containing mat.

In an embodiment, ultra-stable cementitious material with nano-molecular veneer includes: 0.1 weight percent to 15 weight percent biomass added to the amorphous phase cementitious material based on the final total weight of the concrete.

The biomass can be a member of the group comprising: rice husks, corn husks, and dung.

In an embodiment, ultra-stable cementitious material with nano-molecular veneer includes: 0.1 wt % to 10 wt % of at least one surfactant to the cementitious material based on the final total weight of the concrete to decrease porosity of aggregate and prevent amorphous phase cementitious material from entering pores of the aggregate.

The surfactant can be a detergent.

In an embodiment, ultra-stable cementitious material with nano-molecular veneer includes: 0.1 weight percent to 5 weight percent of a re-dispersible powder polymer based on the final total weight of the concrete.

The re-dispersible powder polymer is selected from the group consisting of silicon, polyurethane dispersion, polyurethane, alkyl carboxylic acid vinyl ester monomer, branched and unbranched alcohol(meth)acrylic acid ester monomer, vinyl aromatic monomer, olefin monomer, diene monomer and vinyl halide monomer or a vinyl acetate ethylene “VAE”.

In an embodiment, ultra-stable cementitious material with nano-molecular veneer includes: 0.1 weight percent to 5 weight percent based on the final total weight of the cementitious material of an acrylic or styrene butadiene rubber (SBR) into the concrete while the re-dispersible powder polymer is added.

In an embodiment, ultra-stable cementitious material with nano-molecular veneer includes: 0.1 wt % to 15 wt % of a reinforcing material based on the final total weight of the concrete.

The reinforcing material comprising at least one of: chopped silica containing fibers; hemp containing fibers; nano-molecular carbon fiber strands; chopped carbon fibers; chopped hydrocarbon fiber; and combinations thereof.

The following definitions are used herein:

The term “aggregate” refers to a wood, perlite, foam beams, glass, calcium carbonate powder, or carbon fiber strands with a particle size no larger than 3 mm.

The term “amorphous phase” refers to a non-crystalline mixture of the final reacted products.

The term “amorphous nano-molecular veneer” refers to a coating bonded to the crystallized portion that has a material which is not visible as crystalline in an X-ray diffraction test, and has a density of molecules which is inert to water molecules.

The term “biomass” refers to organic materials such as wood flour, straw, ground pecan shells, and ground up bagasse.

The term “cementitious construction material” refers to a board or structure that is used for structural assembly to form facilities, offices, barns, homes, fences, and marine quarters for use on a ship or oil platform offshore.

The term “crystallized portion” refers to a segment of the created cementitious construction material with activation energies of 70 kilojoules per mole, having a monoclinic crystalline structure which in this invention includes magnesium oxychloride.

The term “crystalline silica” refers to silica molecules, such as sand, in a crystalline phase, similar to glass.

The term “dispersible polymer” is a water dispersible ethylene-vinyl acetate copolymer.

The term “encapsulating” refers to the creation of a nano-molecular veneer over surfaces of the crystals wherein the surface coating can be connected, such as sandpaper which comprises many silica particles adhered to a substrate with very little space between the silica particles. The dendritic nature of the plurality of crystals provide a coating that may be continuous or have small gaps.

The term “fibers” refers to needle-like materials that do not exceed 3 mm in length, but could include longer fibers woven into a mat.

The term “gel phase” refers to a phase in which molecules attract to each other without bonding in a slurry.

The term “insoluble in water” refers to a compound that will not go into solution or degrade when exposed to water between ambient temperature and 60 degrees C. for 0 hours to 48 hours.

The term “magnesium chloride in a water” refers to a liquid containing anhydrous magnesium chloride salt such as a water containing an anhydrous magnesium chloride salt with from 20 to 35 weight percent salt in the water which can be distilled water, dirty water containing particulates and non-volatile organic matter, or clean tap water.

The term “magnesium oxide” refers to the powder form of MgO with from 80% to 98% purity, the balance being calcium carbonate, quartz, or iron oxide or similar impurities naturally found in magnesite.

The term “magnesium phosphate crystals” refers to the crystals formed by the reaction of magnesium oxide with phosphoric acid or phosphorous acid.

The term “nano-molecular elements” refers to the newly identified, insoluble in water, non-crystalline, phosphorous-containing species; identifiable with scan electron microscope (SEM) with elemental analysis. This material will not show up as a phosphorous containing species on XRAY DIFFRACTION.

The term “phosphoric acid” refers to a concentrate of H₃PO₄ with a density of 1.1 g/ml to 1.85 g/ml.

The term “phosphorous acid” refers a concentrate of H₃PO₃ with a density of 1.1 g/ml to 1.65 g/ml.

The term “plurality of crystals” refers to the magnesium oxychloride crystals which form from part of the amorphous phase.

The term “predetermined temperature for the water” refers to a temperature from ambient temperature to 90 degrees C.”.

The term “preset period of time” refers to a window of time from 10 hours to 90 hours, and specifically includes from 24 hours to 72 hours.

The phrase “protects the plurality of crystals from degradation in water” refers to the nano-molecular veneer making the strength loss lower than it would be without the nano-molecular veneer when the cementitious material is exposed to water between ambient temperature and 60 degrees C. for 0-48 hours.

The term “substantially free” refers to a less than 3 weight percent content of crystalline silica based on x-ray diffraction testing in the cementitious construction material.

The term “surface area” refers to the surface area as tested using the BET theory methodology.

The term “veneer” refers to a chemically bonded protective layer on the crystallized portion of the amorphous phase configured to resist water which can be elevated to 60 degrees C. for extended periods of time.

The term “water” refers to H₂O with impurities of less than 0.5 weight percent.

The aggregate includes particles based on a final total weight of the cementitious material, having a diameter from 1 nm to 10 mm.

The aggregate contains at least one of: wood, perlite, styrene based foam beads, calcium carbonate powder, glass particulate, and combinations thereof.

The cementitious material with aggregate is blended to the amorphous phase with from 0.1 wt % to 2 wt % of a reinforcing material based on a final total weight of the cementitious material.

The reinforcing material can be a non-woven or woven silica containing mat, a non-woven, or woven hydrocarbon containing mat.

In other embodiments, the reinforcing material can be chopped silica containing fibers; hemp containing fibers; nano-molecular carbon fiber strands; chopped carbon fibers; chopped hydrocarbon fiber; and combinations thereof.

The amorphous phase cementitious material containing aggregate can be poured over the reinforcing material enabling a portion of the amorphous phase cementitious material to grow a plurality of crystals, each crystal having a MW within the range of 280 to 709, the amorphous phase cementitious material encapsulating the plurality of crystals.

A majority of stabilizing material with a phosphorus-containing compound can be consumed into a nano-molecular veneer while increasing surface area of the plurality of crystals by 2% to 49% during curing, and wherein the nano-molecular elements of the cured nano-molecular veneer are insoluble in water and the cured nano-molecular veneer protects the plurality of crystals from degradation in water at temperatures from 20 degrees to 60 degrees Celsius for from 24 hours to 56 days of the formed cementitious material.

In embodiments of the cementitious material, 0.1 weight percent to 15 weight percent biomass can be added to the amorphous phase cementitious material based on the final total weight of the cementitious material.

In embodiments of the cementitious material, 0.1 wt % to 10 wt % of at least one surfactant is added to the cementitious material based on the final total weight of the cementitious material to decrease porosity of aggregate and prevent amorphous phase cementitious material from entering pores of the aggregate.

In embodiments of the cementitious material, 0.1 weight percent to 5 weight percent of a re-dispersible powder polymer based on the final total weight of the cementitious material can be incorporated in the amorphous phase cementitious material.

In embodiments of the cementitious material, the re-dispersible powder polymer can be selected from the group consisting of acrylic, silicon, polyurethane dispersion, polyurethane, alkyl carboxylic acid vinyl ester monomer, branched and unbranched alcohol(meth)acrylic acid ester monomer, vinyl aromatic monomer, olefin monomer, diene monomer and vinyl halide monomer.

In embodiments of the cementitious material, 0.1 weight percent to 5 weight percent based on the final total weight of the cementitious material of an acrylic or styrene butadiene rubber (SBR) can be blended into the amorphous cementitious material with the re-dispersible powder polymer.

In embodiments of the cementitious material, 0.1 weight percent to 5 weight percent based on the final total weight of the cementitious material of a re-dispersible polymer powder can be added to the amorphous cementitious material, wherein the re-dispersible polymer powder is a member of the group consisting of: a vinyl ethylene ester and ethylene, a vinyl laurate vinyl chloride copolymer, a vinyl ester monomers, (meth)acrylate monomer, a vinyl aromatic monomer, an olefin monomer. a 1,3-diene monomer, a vinyl halide monomer, a homopolymer or copolymer derived from one or more monomers selected from the group consisting of a vinyl acetate, a vinyl ester of an alpha-branched monocarboxylic acids having from 9 to 11 carbon atoms, a vinyl chloride, an ethylene, a methyl acrylate, a methyl methacrylate, an ethyl acrylate, an ethyl methacrylate, a propyl acrylate, a propyl methacrylate, an n-butyl acrylate, a n-butyl methacrylate, an 2-ethylhexyl acrylate.

The invention relates to a building with an exterior building surface covered with the cementitious material of the formulations of the independent claims of this application.

FIG. 1A shows the steps of the invention.

The process for making a cementitious construction material as step 100: forming a gel phase by blending together magnesium oxide and magnesium chloride in water.

Step 110 can involve adding at least one of: a phosphorous acid and a phosphoric acid to the gel phase while forming an amorphous phase.

Step 120 can require adding from 2 weight percent to 30 weight percent of aggregate to the amorphous phase based on a total final weight of the cementitious construction material.

Step 130 can involve crystallizing a portion of the amorphous phase into a plurality of crystals generating nano-molecular elements that project from the plurality of crystals, encapsulating the plurality of crystals, forming a nano-molecular veneer without detectable magnesium phosphate crystals while increasing surface area of the plurality of crystals by 2% to 49%, and wherein the nano-molecular elements of the nano-molecular veneer are insoluble in water and the nano-molecular veneer protects the plurality of crystals from degradation in water at a predetermined temperature for a preset period of time.

In embodiments, the process for making a cementitious construction material can include adding from 0.1 weight percent to 15 weight percent biomass to the gel phase based on the total final weight of the cementitious construction material.

In embodiments, the process for making a cementitious construction material can involve adding from 0.1 weight percent to 5 weight percent of a dispersible polymer to the gel phase based on the total final weight of the cementitious construction material.

FIG. 1B shows a first embodiment incorporating the fewest steps needed to make the cementitious material.

Step 200 can include forming from 35 wt % to 79.9 wt % of a cementitious material based on the final total weight of the tile backer board.

Step 201 can involve blending from 29 wt % to 40 wt % of a magnesium oxide dry powder containing 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the cementitious material into 14 wt % to 18 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

Step 202 can involve mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water forming a liquid suspension while minimizing adding gas into the liquid suspension.

Step 204 can involve adding from 0.1 wt % to 10 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

Step 206 can involve reacting during a preset unit of time, the mixed liquid suspension into an amorphous phase cementitious material.

Step 208 can involve blending to the amorphous phase cementitious material from 0.1 wt % to 30 wt % of an aggregate comprising particles based on a final total weight of the tile backer board, having a diameter from 1 nm to 10 mm, wherein the aggregate comprises at least one of: wood, perlite, styrene based foam beads, calcium carbonate powder, glass particulate, and combinations thereof.

Step 210 can involve pouring the flowable concrete over from 0.1 wt % to 2 wt % of a reinforcing material based on a final total weight of the tile backer board forming a reinforced concrete.

Step 212 can involve forming during a preset unit of time, in a portion of the amorphous phase cementitious material a plurality of crystals of a defined Molecular Weight from the amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals.

Step 214 can include testing the formed tile backer board for stability in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

FIG. 1C depicts additional steps to be used with the embodiment of FIG. 1A to make the cementitious material.

FIG. 1C depicts:

Step 220 can include adding from 0.1 wt % to 15 wt % biomass to the amorphous phase cementitious material based on the final total weight of the tile backer board.

Step 222 can include adding from 0.1 wt % to 10 wt % of at least one surfactant which is added to the cementitious material based on the final total weight of the tile backer board to decrease porosity of aggregate and prevent amorphous phase cementitious material from entering pores of the aggregate.

Step 224 can include adding from 0.1 weight percent to 5 weight percent of a re-dispersible powder polymer based on the final total weight of the tile backer board into the amorphous phase cementitious material.

Step 226 can include blending from 0.1 weight percent to 5 weight percent of an acrylic or styrene butadiene rubber (SBR) based on the final total weight of the tile backer board into the amorphous cementitious material with the re-dispersible powder polymer.

FIG. 1D shows steps of another embodiment to make the cementitious material.

Step 250 can include forming from 55 wt % to 99.8 wt % of a cementitious material based on the final total weight of the tile backer board.

Step 252 can include forming from 55 wt % to 99.8 wt % of a cementitious material by blending 29 wt % to 40 wt % of a magnesium oxide dry powder containing from 80 wt % to 98 wt % of magnesium oxide based on a final total weight of the based on the cementitious material with from 14 wt % of 18 wt % of a magnesium chloride dissolved in water based on based on the final total weight of the cementitious material, to form a liquid suspension.

Step 254 can involve adding from 0.1 wt % to 10 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the liquid suspension.

Step 256 can include allowing the liquid suspension to react into an amorphous phase cementitious material during a preset period of time.

Step 258 can involve adding from 0.1 wt % to 30 wt % of an aggregate based on the total weight of the tile backer board to the amorphous phase cementitious material.

Step 260 can involve adding from 0.1 wt % to 15 wt % of a reinforcing material based on the final total weight of the tile backer board, to the amorphous phase cementitious material, wherein the reinforcing material is at least one of: chopped silica containing fibers; hemp containing fibers; nano-molecular carbon fiber strands; chopped carbon fibers; chopped hydrocarbon fiber; and combinations thereof.

Step 262 can involve growing a portion of the amorphous phase cementitious material grows a plurality of crystals, each crystal having a MW within the range of 283 to 709, the amorphous phase cementitious material encapsulating the plurality of crystals, wherein a majority of stabilizing material with a phosphorus-containing compound are consumed into a nano-molecular veneer while increasing surface area of the plurality of crystals by 2% to 49% during curing, and wherein the nano-molecular elements of the cured nano-molecular veneer are insoluble in water and the cured nano-molecular veneer protects the plurality of crystals from degradation in water at temperatures from 20 degrees to 60 degrees Celsius for from 24 hours to 56 days of the formed tile backer board.

In embodiments, the cementitious construction material can create a nano-molecular veneer with a thickness from 1 microns to 3 microns.

In embodiments, the cementitious construction material can be used to create a cementitious construction material configured to support a load of at least 2.5 pounds per square foot.

In embodiments, the cementitious construction material produces product can be used to create a home, an office, a warehouse, a shed, a dock, artwork, aqueducts, or another load supporting structure.

In embodiments, the water is a brine or similar salt solution with a concentration of 2% to 30% salt.

In embodiments, the cementitious construction material can contain fibers.

In variations of the cementitious construction material, prior to crystallizing the amorphous phase, an additional substrate can be introduced and coated with the cementitious construction material having oriented strand board, plywood, waterproof membrane, concrete, and wood, and coated with the amorphous phase increasing fire resistance and stability in hot water.

The cementitious construction material can include least one surfactant added to the amorphous phase to decrease porosity of aggregates and prevent amorphous phase from entering pores of the aggregates.

The surfactants can be any molecule that reduces the surface porosity of the aggregates being used in the cement.

In embodiments, the amorphous phase can be crystallized using a temperature from 40 to 50 degrees C. for a period of time from 3 to 24 hours, at a relative humidity from 30 to 100 percent.

In embodiments, the cementitious construction material can be formed using an exothermic reaction, such as generating 10 to 15 degrees of heat for the duration of the reaction.

In embodiments, the cementitious construction material gel phase can be formed using intimate mixing for at least 3 minutes prior to adding aggregate.

FIG. 2 shows diffractograms of cured samples produced from X-ray diffraction at 28 degrees C. The major 5 phase peaks are labelled. The four upper quadrants are post phosphoric acid treatment and the bottom quadrant is pre phosphoric acid treatment.

The importance of this FIG. 2 is the area under the peaks.

EXAMPLE 1

A cementitious construction cementitious material:

The cementitious material has a 78% crystallized portion with 12% of an amorphous nano-molecular veneer substantially free of crystalline silica.

To create the cementitious material, first a gel phase is formed by blending together magnesium oxide powder with a purity of 85% by weight and a magnesium chloride in a brine with density of 1.26.

The magnesium oxide is blended in a weight ratio of 2:1 with the magnesium chloride based on the total final weight of the cementitious construction material.

Next, from 20 weight percent of aggregate from wood is added to the gel phase forming the amorphous phase.

To the amorphous phase, 5 weight percent of phosphoric acid is added based on the total final weight of the cementitious construction material.

To complete forming of the cementitious material, 65% of the amorphous phase is crystallized by extruding the amorphous phase between two layers of fiberglass on a carrier sheet. The sandwich-like material is cured at 45-55 degrees C. for 12-24 hours at a relative humidity greater than 55% creating a board with a thickness of 12 mm.

A nano-molecular veneer is formed over the crystallized portion with a veneer thickness of 1 micron encapsulating the portion of the crystallized portion without producing detectable magnesium phosphate. The nano-molecular veneer has a 30% increase in surface area as compared to veneer-free crystallized portions.

The final crystallized portion with nano-molecular veneer is configured to resist degradation in water having a temperature at 60 degrees C. for 48 hours.

EXAMPLE 2

The novel cementitious material is formed by combining 34 wt % of a magnesium oxide dry powder containing 85 wt % purity of magnesium oxide based on a final total weight of the cementitious material.

The magnesium oxide used has a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles are less than or equal to about 40 microns.

16 wt % of a magnesium chloride was dissolved in water based on a final total weight of the cementitious material. The magnesium chloride in aqueous solution was: 29 wt % of a magnesium chloride aqueous solution. The magnesium oxide and the magnesium chloride in water reacted to form a liquid suspension.

1.3 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material was then mixed with the liquid suspension and the mixture reacted into an amorphous phase cementitious material.

The stabilizing material with the phosphorus-containing compound was phosphoric acid (B) based on the final total weight of the cementitious material, wherein the phosphoric acid consisted of an aqueous solution of 85 wt % of a concentrate of H₃PO₄. The mixture reacted into an amorphous phase cementitious material.

The amorphous phase cementitious material grows a plurality of crystals, each crystal having a MW of 530 generating nano-molecular elements that project from the plurality of crystals, encapsulating the plurality of crystals, wherein a majority of stabilizing material with a phosphorus-containing compound are consumed into the non-molecular veneer while increasing surface area of the plurality of crystals by 49%, and wherein the nano-molecular elements of the nano-molecular veneer are insoluble in water and the nano-molecular veneer protects the plurality of crystals from degradation in water at 60 degrees Celsius for 24 hours forming the cementitious material.

EXAMPLE 3

The cementitious material of this example has 35 wt % of a magnesium oxide dry powder containing 80 wt % purity of magnesium oxide based on a final total weight of the cementitious material.

The magnesium oxide used has a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles are less than or equal to about 40 microns.

15 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material was mixed with the magnesium oxide,

In this example, the magnesium chloride in aqueous solution was a 27 wt % a magnesium chloride aqueous solution. The magnesium oxide and the magnesium chloride in water were mixed and react to form a liquid suspension.

2.5 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material was mixed with the liquid suspension, the mixture reacted into an amorphous phase cementitious material, the stabilizing material with the phosphorus-containing compound contained a phosphorous acid (A) based on the final total weight of the cementitious material. The phosphorous acid consisted of an aqueous solution of 60 wt % of a concentrate of H₃PO₃.

A portion of the amorphous phase cementitious material grew a plurality of crystals, developed with each crystal having a MW of 283, 413, 530, or 709, generating nano-molecular elements that projected from the plurality of crystals, encapsulating the plurality of crystals.

A majority of phosphorous-containing compounds from the stabilizing material with a phosphorus-containing compound were consumed into the non-molecular veneer while increasing surface area of the plurality of crystals by 2 to 49%.

The nano-molecular elements of the nano-molecular veneer were insoluble in water and the nano-molecular veneer protected the plurality of crystals from degradation in water at 60 degrees Celsius for 24 hours as the cementitious material.

FIGS. 3A-3H show many samples of the formulation of the cementitious material and their associated physical properties.

Sample 1 contains 29 wt % of a magnesium oxide dry powder based on a final total weight of the cementitious material was used. The magnesium oxide dry powder containing 85 wt % purity of magnesium oxide.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 14 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 1, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 0.1 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 1, the stabilizing material with the phosphorus-containing compound was a phosphorous acid based on the final total weight of the cementitious material, wherein the phosphorous acid consists of an aqueous solution of 60 wt % of a concentrate of H₃PO₃.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

The flowable, uncured cementitious material was then poured on a mold to cure and form a cement.

For this Sample 1, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by 2% to 20 m²/g.

The cured material of Sample 1 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 2

Sample 2 contains 40 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 18 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 2, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 10 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 2, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

The flowable, uncured cementitious material was then poured on a mold and cured, forming a cement.

For this Sample 2, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by 49% to 29 m²/g.

The cured material of Sample 2 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 3

Sample 3 contains 32 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 17 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 3, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 0.1 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of cementitious material the mixed liquid suspension.

For Sample 3, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

The reinforcing component was a non-woven silica-containing mat. The reinforcing component was 0.1 wt % based on the total final weight of the cementitious material.

For this Sample 3, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by 2% to 20 m²/g.

The cured material of Sample 3 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 4

Sample 4 contains 31 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 16 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 4, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 1 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 4, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

The reinforcing component was 2 wt % chopped silica fibers based on the total final weight of the cementitious material.

For this Sample 4, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by 23% to 24 m²/g.

The cured material of Sample 4 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 5

Sample 5 contains 32.5 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 17.5 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 5, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 1.75 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 5, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

Sample 5 contains 0.1 wt % of aggregate component known as wood:perlite:styrene based foam beads in a 30:8:1 ratio based on the total final weight of the cementitious material was added into the amorphous phase cementitious material forming a flowable concrete.

The flowable, uncured concrete was then poured on a mold and cured to make a finished concrete.

For this Sample 5, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by more than 38% to 27 m²/g.

The cured material of Sample 5 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC. Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 6

Sample 6 contains 33 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 18 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 6, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 2.5 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material the mixed liquid suspension.

For Sample 6, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

Sample 6 contains 30 wt % of aggregate component of wood:perlite:styrene based foam beads in a 30:8:1 ratio based on the total final weight of the cementitious material was added into the amorphous phase cementitious material forming a flowable concrete.

The flowable, uncured concrete was then poured into a mold and cured to make a finished concrete.

For this Sample 6, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by more than 49% to 29 m²/g.

The cured material of Sample 6 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 7

Sample 7 contains 33 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 19 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 7, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 3.75 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 7, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

Sample 7 contains a biomass of 0.1 weight percent based on the total final weight of the cementitious material. The biomass of this example was rice husks.

For this Sample 7, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by 49% to 29 m²/g.

The cured material of Sample 7 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 8

Sample 8 contains 32 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 17 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 7, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 5 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 8, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

Sample 8 contains 15 wt % of biomass based on the total final weight of the cementitious material was added into the amorphous phase cementitious material forming a flowable concrete. The biomass was corn husks.

The flowable, uncured concrete was then poured into a mold, the finished material forming a concrete.

For this Sample 8, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by more than 44% to 28 m²/g.

The cured material of Sample 8 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 9

Sample 9 contains 35 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 16 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 9, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 6.25 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 9, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

0.1 weight percent of a surfactant, namely a detergent was added to the amorphous phase cementitious material based on the final total weight of the cementitious material.

The flowable, uncured concrete was then poured into a mold forming a finished concrete.

For this Sample 9, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by 23% to 24 m²/g.

The cured material of Sample 9 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 10

Sample 10 contains 30 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 18 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 10, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 7.5 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 10, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

Sample 10 contains 10 wt % of sodium stearate as a surfactant, based on the total final weight of the cementitious material was added into the amorphous phase cementitious material forming a flowable concrete.

The flowable, uncured concrete was then poured in a mold forming a finished concrete.

For this Sample 10, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by more than 38% to 27 m²/g.

The cured material of Sample 10 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 11

Sample 11 contains 33 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 15 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 11, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 8.75 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 11, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

0.1 weight percent of re-dispersible polymer, namely vinyl acetate ethylene (VAE) was added to the amorphous phase cementitious material based on the final total weight of the cementitious material.

The flowable, uncured concrete was then poured into a mold forming a finished concrete.

For this Sample 11, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by more than 49% to 29 m²/g.

The cured material of Sample 11 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017.

Sample 12

Sample 12 contains 32 wt % of a magnesium oxide dry powder containing 85 wt % of magnesium oxide based on a final total weight of the cementitious material was used.

The magnesium oxide had a surface area ranging from 5 meters²/gram to 50 meters²/gram and an average particle size ranging from about 0.3 to about 90 microns wherein more than about 90% by weight magnesium oxide particles were less than or equal to about 40 microns.

The magnesium oxide was blended with 19 wt % of a magnesium chloride dissolved in water based on a final total weight of the cementitious material.

For Sample 12, the magnesium chloride in aqueous solution was a 28 wt % magnesium chloride aqueous solution.

After 3 minutes of mixing with a planetary mixer, the magnesium oxide and the magnesium chloride in water form a liquid suspension while minimizing adding gas into the liquid suspension.

For this sample, the next step involved adding 10 wt % of a stabilizing material with a phosphorus-containing compound based on a final total weight of the cementitious material to the mixed liquid suspension.

For Sample 12, the stabilizing material with the phosphorus-containing compound was a phosphoric acid based on the final total weight of the cementitious material, wherein the phosphoric acid consists of an aqueous solution of 80 wt % to 90 wt % of a concentrate of H₃PO₄.

The liquid suspension with stabilizing material was permitted to react into an amorphous phase cementitious material for a period of time of 2 minutes.

Sample 12 contains 5 wt % of vinyl acetate ethylene based on the total final weight of the cementitious material was added into the amorphous phase cementitious material forming a flowable concrete.

The flowable, uncured concrete was then poured into a mold forming finished concrete.

For this Sample 12, a portion of the amorphous phase cementitious material formed a plurality of crystals, each crystal is known as a “Magnesium Oxychloride Cement Crystals” having a MW of 530.7 with amorphous non-crystalline nano-molecular cementitious material encapsulating the plurality of crystals, creating a nano-molecular veneer without detectable phosphorus-containing compound while increasing surface area of the plurality of crystals by 49% to 29 m²/g.

The cured material of Sample 12 formed a cementitious material which as stable in water at 60 degrees Celsius for 24 hours using the Jet Products, LLC Warm Water Stability Test as authenticated by Clemson University Chemical Engineering Department in 2017. 

What is claimed is:
 1. A cementitious material that is the product of: (i) blending a) 29 wt. % to 40 wt. %, based on the final total weight of the cementitious material, of a magnesium oxide dry powder containing 80 wt. % to 98 wt. % of magnesium oxide, the magnesium oxide powder having a surface area of from 5 m²/g to 50 m²/g and an average particle size of from about 0.3 μm to about 90 μm, and wherein more than about 90 wt. % of the particles of the magnesium oxide powder have a particle size of less than or equal to about 40 μm, with b) 14 wt. % to 18 wt. %, based on the final total weight of the cementitious material, of an aqueous solution of magnesium chloride, the aqueous solution of magnesium chloride comprising 20 wt. % to 30 wt. % of magnesium chloride, and reacting the magnesium oxide and the magnesium chloride to form a liquid suspension; (ii) mixing the liquid suspension for from 2 minutes to 10 minutes; (iii) adding 0.1 wt. % to 10 wt. %, based on the final total weight of the cementitious material, of a stabilizing material to the mixed liquid suspension, wherein the stabilizing material is: 1) an aqueous solution comprising 55 wt. % to 65 wt. % of phosphorous acid (H₃PO₃); or 2) an aqueous solution comprising 80 wt. % to 90 wt. % of phosphoric acid (H₃PO₄); and (iv) allowing the liquid suspension with the stabilizing material to react for from 1 minute to 4 minutes to form an amorphous phase cementitious material; wherein a portion of the amorphous phase cementitious material grows a plurality of crystals, each crystal having a molecular weight of from 280 to 709 and being encapsulated by the amorphous phase cementitious material; wherein a majority of the stabilizing material is consumed during curing into a nano-molecular veneer over the crystals while increasing the surface area of the plurality of crystals by 2% to 49%; and wherein the nano-molecular veneer is insoluble in water and protects the plurality of crystals from degradation in water at temperatures of from 20° C. to 60° C. for from 24 hours to 56 days.
 2. The cementitious material of claim 1, further comprising 0.1 wt. % to 30 wt. %, based on the final total weight of cementitious material, of an aggregate comprising particles having a diameter from 1 nm to 10 nm, wherein the aggregate comprises at least one selected from the group consisting of wood, perlite, styrene-based foam beads, calcium carbonate powder, and glass particulates.
 3. The cementitious material of claim 1, further comprising 0.1 wt. % to 2 wt. %, based on the final total weight of the cementitious material, of a reinforcing material comprising a non-woven or woven silica-containing mat or a non-woven or woven hydrocarbon-containing mat.
 4. The cementitious material of claim 1, further comprising 0.1 wt. % to 15 wt. %, based on the final total weight of the cementitious material, of biomass.
 5. The cementitious material of claim 4, wherein the biomass is selected from the group consisting of rice husks, corn husks, and dung.
 6. The cementitious material of claim 2, further comprising 0.1 wt. % to 10 wt. %, based on the final total weight of the cementitious material, of at least one surfactant that is effective to decrease the porosity of the aggregate and to prevent the amorphous phase cementitious material from entering pores of the aggregate.
 7. The cementitious material of claim 6, wherein the surfactant is a detergent.
 8. The cementitious material of claim 2, further comprising 0.1 wt. % to 5 wt. %, based on the final total weight of the cementitious material, of a redispersible powder polymer.
 9. The cementitious material of claim 8, wherein the redispersible powder polymer is selected from the group consisting of a silicone, a polyurethane, a polyurethane dispersion, a polymer of an alkyl carboxylic acid vinyl ester monomer, a polymer of a branched or unbranched alcohol ester of (meth)acrylic acid monomer, a polymer of a vinyl aromatic monomer, a polyolefin, a polydiene, a polyvinyl halide, and a copolymer of vinyl acetate and ethylene.
 10. The cementitious material of claim 8, further comprising 0.1 wt. % to 5 wt. %, based on the final total weight of the cementitious material, of an acrylic or a styrene-butadiene rubber.
 11. The cementitious material of claim 1, further comprising 0.1 wt. % to 15 wt. %, based on the final total weight of the cementitious material, of at least one reinforcing material selected from the group consisting of chopped silica-containing fibers, hemp-containing fibers, nano-molecular carbon fiber strands, chopped carbon fibers, and chopped hydrocarbon fibers. 